DETERMINATION OF THE MAGNETIC PROPERTIES OF MANGANESE FERRITE BY THE COPRECIPITATION METHOD AT DIFFERENT pH CONCENTRATIONS
摘要
Manganese ferrite (MnFe2O4) as a magnetic material was greatly affected by several parameters formed during the synthesis process. One of the parameters necessary in the coprecipitation synthesis process is the pH concentration in the titration process. The pH variations can affect the magnetic properties of MnFe2O4, and it was very interesting to review the effect of pH on its magnetic properties of. Manganese ferrite was synthesized by using the coprecipitation method with pH being equal to 8, 10, and 12 and sintered at a temperature of 1000°C for 3 h. Manganese ferrite nanopowder that had been synthesized was analyzed by using XRD, SEM, and VSM. The characterization process was conducted with both sintered and unsintered manganese ferrite. The XRD results indicated that the unsintered sample at all values of pH was amorphous, while the sintered samples at all pH values showed that a single phase was formed in a lattice with dimensions 59.48 nm, 41.60 nm, and 29.72 nm for pH equal to 8, 10, and 12. The SEM testing showed that the structure of all samples was homogeneous. Although the bulk size of unsintered samples was smaller and more homogeneous than that of sintered samples, the results showed that all unsintered samples had similar values and superparamagnetic properties. However, unlike the sintered sample, which was much more homogeneous, there was transition from the superparamagnetic properties to paramagnetic properties at pH equal to 12. Thus, it was found that the higher the pH level, the smaller the crystallite size.
-
Muhammad Alief, Puspitasari Poppy, Andoko , Properties of soft magnetic material SmCo5 synthesized using low-temperature sol-gel method, INTERNATIONAL CONFERENCE ON BIOLOGY AND APPLIED SCIENCE (ICOBAS), 2120, 2019. Crossref
-
Time Dependence on Magnetic Properties of Nanomaterial Manganese–Zinc Ferrite (Mn0.8Zn0.2Fe2O4) by Co-Precipitation Method, Nanosistemi, Nanomateriali, Nanotehnologii, 17, 2, 2019. Crossref
-
Amjed Muhammad Ahsan, Wu Xiange, Ali Imran, Naz Iffat, Dai Min, Tehrim Aafia, Niaz Waqas, Javaid Sheikh Fahad, Peng Changsheng, Surface decoration and characterization of solar driven biochar for the removal of toxic aromatic pollutant, Journal of Chemical Technology & Biotechnology, 96, 8, 2021. Crossref