Volume 29, 2019 Volume 28, 2018 Volume 27, 2017 Volume 26, 2016 Volume 25, 2015 Volume 24, 2014 Volume 23, 2013 Volume 22, 2012 Volume 21, 2011 Volume 20, 2010 Volume 19, 2009 Volume 18, 2008 Volume 17, 2007 Volume 16, 2006 Volume 15, 2005 Volume 14, 2004 Volume 13, 2003 Volume 12, 2002 Volume 11, 2001 Volume 10, 2000 Volume 9, 1999 Volume 8, 1998 Volume 7, 1997 Volume 6, 1996 Volume 5, 1995 Volume 4, 1994 Volume 3, 1993 Volume 2, 1992 Volume 1, 1991

Atomization and Sprays

DOI: 10.1615/AtomizSpr.v15.i2.40
pages 169-180

ATOMIZATION OF VISCOUS MELTS

H. Lohner
Department of Chemical Engineering, University of Bremen, Bremen, Germany
C. Czisch
University Bremen, Chemical Engineering Departmen, Badgasteiner Str. 3 D-28359 Bremen, Germany
P. Schreckenberg
Department of Chemical Engineering, University of Bremen, Bremen, Germany
Udo Fritsching
Department of Particles and Process Engineering, University of Bremen; Foundation Institute of Materials Science, Badgasteiner Str. 3, D-28359 Bremen, Germany
Klaus Bauckhage
Chemical Engineering Department, University of Bremen, Bremen, Germany

RÉSUMÉ

Specific melt types have high viscosity and comparably low surface tension. Therefore, conventional twin-fluid atomization of these viscous melts for powder production often results not in spherical particles but in a great amount of fiber material. In this investigation, viscous mineral melts are atomized in a pilot plant by means of hot gases for spherical particle granulation. Experimental results show that an almost fiber-free product (97% spherical powder) can be obtained. Usually, the atomization process is controlled by the gas pressure only (here before the expansion in the atomizer nozzle). For constant atomization pressure the mass median diameter of the powder yield decreases with increasing atomization gas temperature.
Numerical simulations of the gas flow field in the atomizer vicinity support the analysis of the melt fragmentation process by obtaining the gas temperature distribution and the gas flow conditions within the atomization process. Simulations for different atomizer nozzle designs and several operating conditions have been realized. From the discussion of the experimental results together with the results of the simulations, the relevant shear process between the melt jet and the atomization gas, characterized by the Reynolds number, can be determined as the main driving mechanism of the atomization and spheroidization process.