THERMAL STABILITY OF TiAlBN and TiN/TiCN COATINGS

A. Raveh
Division of Chemistry, NRC-Negev, P.O. Box 9001, Beer-Sheva 84190; and Ben-Gurion University, P.O. Box 653, Beer-Sheva 84105, Israel
I. Zukerman
Ben-Gurion University, P.O. Box 653, Beer-Sheva 84105, Israel
R. Z. Shneck
Ben-Gurion University, P.O. Box 653, Beer-Sheva 84105, Israel
R. Avni
Euro-Consultants (Israel), 10 Dov Friedman St. Ramat Gan, Israel
I. Fried
Euro-Consultants (Israel), 10 Dov Friedman St. Ramat Gan, Israel

要約

Thermal stability of TiAlBN and TiN/TiCN hard coatings was studied by evaluating the stress-temperature curves and the wear resistance after annealing up to 1123 K. The microstructure, phase composition and hardness were studied prior and after annealing.
Prior to annealing, a correlation between the residual stress and hardness was observed. After annealing, the compressive stresses of the TiAlBN coatings decreased from 1.0 GPa to less than 0.2 GPa, while the hardness remained constant or increased from ~10 GPa to ~25 GPa. The hardness increase of the coatings after annealing is related to the self-hardening effect.
The effect of the plasma nitriding mode prior to the deposition of 3 μm thick TiCN or TiN/TiCN coatings on the wear resistance of the duplex-treated coating (nitriding and deposition) was studied. The stability of the wear resistance of the duplex treated-coating was also examined after one hour of annealing at 1123 K. It was found that the plasma-nitrided layer in the duplex treatment maintains the wear resistance stability of the annealed duplex-treated hard coatings.


Articles with similar content:

THERMAL SHOCK BEHAVIOUR OF CORDIERITE CERAMIC FILTER FROM NANOSIZE SEPOLITE
ICHMT DIGITAL LIBRARY ONLINE, Vol.0, 2011, issue
Esin Gunay, Meryem Sariguzel
NANOMODIFIED DISPERSED PARTICLES- AND SYNTHETIC FIBERS-FILLED EPOXY COMPOSITE MATERIALS FOR THE METAL- POLYMER TRIBOSYSTEMS OF TRANSPORT VEHICLES
Nanoscience and Technology: An International Journal, Vol.8, 2017, issue 1
A. V. Buketov, Sergey O. Smetankin, Dmitriy O. Zinchenko
AUSTENITIC STEEL SURFACE ALLOYED WITH ZIRCONIUM USING COMPRESSION PLASMA FLOW
High Temperature Material Processes: An International Quarterly of High-Technology Plasma Processes, Vol.16, 2012, issue 4
Valiantsin M. Astashynski, Nikolai N. Cherenda, E. A. Kostyukevich, A. M. Kuzmitski, A. H. Sari, Vladimir V. Uglov, Yu. A. Petukhou
Alumina coatings from aluminium electrodeposited in molten salts
Advances in Molten Salts, Vol.0, 1998, issue
Pr. V. Hasthorpe, Ir. S. Delhaye
COATING DEPOSITION BY THERMAL SPRAY PROCESSES
Annual Review of Heat Transfer, Vol.20, 2017, issue 1
Sanjeev Chandra