Thermal cycling behavior of Yttria Stabilized Zirconia and Lanthanum Zirconate as graded and bilayer EB-PVD thermal barrier coatings

K. Bobzin
Surface Engineering Institute (IOT), RWTH University of Technology Aachen, Augustinerbach 4-22, 52066 Aachen, Germany
Erick Lugscheider
Werkstoffwissenschaften Lehr und Forschungsgebeit der RWTH Jiilicher Sir. 342-352 52070 Aachen; Surface Engineering Institute (IOT), RWTH University of Technology Aachen, Augustinerbach 4-22, 52066 Aachen, Germany
N. Bagcivan
Surface Engineering Institute (IOT), RWTH University of Technology Aachen, Augustinerbach 4-22, 52066 Aachen, Germany

要約

Traditionally Yttria partially stabilized Zirconia (YPSZ) coatings are used as thermal barrier coatings (TBCs) on chambers. More and more often, they are applied on turbine blades. Investigations on some various materials with perovskite, spinel and pyrochlore structures have shown a great potential of Lanthanum Zirconate (pyrochlore) as thermal barrier coatings. In this work, Lanthanum Zirconate has been developed as a TBC using Electron Beam Physical Vapour Deposition (EB-PVD). TBCs deposited by EB-PVD exhibit a columnar grain microstructure, which is able to better balance the difference in thermal expansion between the base material and TBC during thermal cycle and hence improved the TBC lifetime. Two different coating architectures were developed for the TBCs. First a bilayer TBC consisting of YSZ and Lanthanum Zirconate was deposited. In the second approach a graded TBC with a transition from YSZ to Lanthanum Zirconate was deposited. The thermal cycling behavior of these coatings on Inconel Alloy 600 was investigated by a thermal cycling test at 1050 °C. Additionally, the coatings were characterized by scanning electron microscopy (SEM) and energy dispersive X-ray analysis (EDX). The results of thermal cycling test showed an increase in the number of cycles before fatigue from 1380 cycles for YSZ to 3390 cycles for the graded YPSZ/Lanthanum Zirconate and 4140 cycles for the bilayer YSZ/Lanthanum Zirconate.


Articles with similar content:

STRUCTURE AND PROPERTIES OF CARBON AND HYDROCARBON FILMS DEPOSITED IN PLASMA OF LOW-PRESSURE ARC AND UNBALANCED DC MAGNETRON
High Temperature Material Processes: An International Quarterly of High-Technology Plasma Processes, Vol.2, 1998, issue 1
V.P. Makarov , I.A. Anisimova, V.P. Anisimov, D.K. Otorbaev
MODELING AND EXPERIMENTAL ANALYSIS OF HEAT TRANSFER FOR POWER ELECTRONIC MODULE INTEGRATED WITH PHASE CHANGE THERMAL MANAGEMENT SYSTEM
International Heat Transfer Conference 16, Vol.10, 2018, issue
Yangang Wang, Yiyi Chen, Yuying Yan, Bo Li
PARAMETERS OF CHEMICAL VAPOR DEPOSITION ON A STRUCTURE AND THE PROPERTIES OF NANOSTRUCTURED TaC COATING ON A CARBON COMPOSITE MATERIAL
Nanoscience and Technology: An International Journal, Vol.5, 2014, issue 3
K. Chuprunov, A. Yudin, V. N. Anikin, Denis Leybo, S. A. Eremin, I. N. Burmistrov, D. V. Kuznetsov
Metal-Oxide Nanoparticles for the Reinforcement of Dental Restorative Resins
Critical Reviews™ in Biomedical Engineering, Vol.28, 2000, issue 3&4
Dan Nicolella, James Lankford, Hong Dixon, Benjamin Furman, Stephen Wellinghoff, H. Ralph Rawls
PROCESS OF FORMATION OF SPHEROIDAL GOLD PARTICLES AND OF NANOPHASES IN AlN−TiB2−TiSi2 COATINGS AFTER ANNEALING WITH SUBSEQUENT IMPLANTATION
High Temperature Material Processes: An International Quarterly of High-Technology Plasma Processes, Vol.19, 2015, issue 2
Katerina Smyrnova, Konrad Kierczynski, Yoshihiko Takeda, Anatoliy Kupchishin, Henryk Komsta, Hiroshi Amekura, Marek Opielak, Bahyt Zhollybekov, Artem Demianenko