Доступ предоставлен для: Guest
Портал Begell Электронная Бибилиотека e-Книги Журналы Справочники и Сборники статей Коллекции
High Temperature Material Processes: An International Quarterly of High-Technology Plasma Processes
SJR: 0.19 SNIP: 0.341 CiteScore™: 0.43

ISSN Печать: 1093-3611
ISSN Онлайн: 1940-4360

Выпуски:
Том 23, 2019 Том 22, 2018 Том 21, 2017 Том 20, 2016 Том 19, 2015 Том 18, 2014 Том 17, 2013 Том 16, 2012 Том 15, 2011 Том 14, 2010 Том 13, 2009 Том 12, 2008 Том 11, 2007 Том 10, 2006 Том 9, 2005 Том 8, 2004 Том 7, 2003 Том 6, 2002 Том 5, 2001 Том 4, 2000 Том 3, 1999 Том 2, 1998 Том 1, 1997

High Temperature Material Processes: An International Quarterly of High-Technology Plasma Processes

DOI: 10.1615/HighTempMatProc.v10.i3.80
pages 445-456

THERMAL STABILITY OF TiAlBN and TiN/TiCN COATINGS

A. Raveh
Division of Chemistry, NRC-Negev, P.O. Box 9001, Beer-Sheva 84190; and Ben-Gurion University, P.O. Box 653, Beer-Sheva 84105, Israel
I. Zukerman
Ben-Gurion University, P.O. Box 653, Beer-Sheva 84105, Israel
R. Z. Shneck
Ben-Gurion University, P.O. Box 653, Beer-Sheva 84105, Israel
R. Avni
Euro-Consultants (Israel), 10 Dov Friedman St. Ramat Gan, Israel
I. Fried
Euro-Consultants (Israel), 10 Dov Friedman St. Ramat Gan, Israel

Краткое описание

Thermal stability of TiAlBN and TiN/TiCN hard coatings was studied by evaluating the stress-temperature curves and the wear resistance after annealing up to 1123 K. The microstructure, phase composition and hardness were studied prior and after annealing.
Prior to annealing, a correlation between the residual stress and hardness was observed. After annealing, the compressive stresses of the TiAlBN coatings decreased from 1.0 GPa to less than 0.2 GPa, while the hardness remained constant or increased from ~10 GPa to ~25 GPa. The hardness increase of the coatings after annealing is related to the self-hardening effect.
The effect of the plasma nitriding mode prior to the deposition of 3 μm thick TiCN or TiN/TiCN coatings on the wear resistance of the duplex-treated coating (nitriding and deposition) was studied. The stability of the wear resistance of the duplex treated-coating was also examined after one hour of annealing at 1123 K. It was found that the plasma-nitrided layer in the duplex treatment maintains the wear resistance stability of the annealed duplex-treated hard coatings.


Articles with similar content:

EXPERIMENTAL INVESTIGATION OF SURFACE HARDNESS AND DRY SLIDING WEAR BEHAVIOR OF AA7050/B4Cp
High Temperature Material Processes: An International Quarterly of High-Technology Plasma Processes, Vol.19, 2015, issue 3-4
P. K. Giridharan, Ranjith Rajamanickam
INFLUENCE OF DC PLASMA PREHEATING ON OXIDE LAYERS FORMED BY FURNACE HEATING ON LOW CARBON STEEL SUBSTRATES AND RESULTING ADHESION/COHESION OF ALUMINA COATINGS
Progress in Plasma Processing of Materials, 2003, Vol.0, 2003, issue
Pierre Lefort, S. Valette, Alain Denoirjean, Pierre Fauchais
NITRIDING OF COMMERCIAL PURE TITANIUM IN THE PLASMA OF FREQUENCY-PULSED NON-SELF-SUSTAINED GLOW DISCHARGE WITH A HOLLOW CATHODE AT LOW PRESSURE
High Temperature Material Processes: An International Quarterly of High-Technology Plasma Processes, Vol.21, 2017, issue 1
E. A. Petrikova, Vladimir V. Denisov, Nikolay N. Koval, Nikolai N. Cherenda, Vitali I. Shymanski, Yurii F. Ivanov, Olga V. Krysina, A. P. Laskovnev, Vladimir V. Uglov
EXPERIMENTAL INVESTIGATION OF STRUCTURE, WEAR, AND EROSION RESISTANCE OF SS316 SUBSTRATE COATED WITH TiC–Al2O3 COMPOSITE BY LASER CLADDING
High Temperature Material Processes: An International Quarterly of High-Technology Plasma Processes, Vol.22, 2018, issue 1
Elango Natarajan, R. Prabu, S. Ramesh
TRANSFORMATIONS OF ARMCO IRON SURFACE ON THERMOKINETIC EXPOSURE TO COMPRESSION PLASMA FLOWS
High Temperature Material Processes: An International Quarterly of High-Technology Plasma Processes, Vol.17, 2013, issue 2-3
Valiantsin V. Astashynski, Iryna N. Rumiantseva