Доступ предоставлен для: Guest
Портал Begell Электронная Бибилиотека e-Книги Журналы Справочники и Сборники статей Коллекции
High Temperature Material Processes: An International Quarterly of High-Technology Plasma Processes
ESCI SJR: 0.176 SNIP: 0.48 CiteScore™: 1.3

ISSN Печать: 1093-3611
ISSN Онлайн: 1940-4360

Выпуски:
Том 24, 2020 Том 23, 2019 Том 22, 2018 Том 21, 2017 Том 20, 2016 Том 19, 2015 Том 18, 2014 Том 17, 2013 Том 16, 2012 Том 15, 2011 Том 14, 2010 Том 13, 2009 Том 12, 2008 Том 11, 2007 Том 10, 2006 Том 9, 2005 Том 8, 2004 Том 7, 2003 Том 6, 2002 Том 5, 2001 Том 4, 2000 Том 3, 1999 Том 2, 1998 Том 1, 1997

High Temperature Material Processes: An International Quarterly of High-Technology Plasma Processes

DOI: 10.1615/HighTempMatProc.2015015698
pages 281-290

ELECTROEXPLOSIVE DOPING OF TITANIUM ALLOY BY BORON CARBIDE AND SUBSEQUENT ELECTRON BEAM PROCESSING

Yurii F. Ivanov
National Research Tomsk Polytechnic University, 30 Lenin Ave., Tomsk, 634050, Russia; Institute of High Current Electronics, Siberian Branch of the Russian Academy of Sciences, 2/3 Akademichesky Ave., Tomsk, 634055, Russia
T. A. Kobzareva
Siberian State Industrial University, 42 Kirov St., Novokuznetsk, 654007, Russia
V. E. Gromov
Sibirian State Industrial University, 42 Kirov St., Novokuznetsk, 654007, Russia
E. A. Budovskikh
Sibirian State Industrial University, 42 Kirov St., Novokuznetsk, 654007, Russia
L. P. Bashchenko
Siberian State Industrial University, 42 Kirov St., Novokuznetsk, 654007, Russia

Краткое описание

VT6 titanium alloy surface modification is carried out by electroexplosive alloying with a plasma formed in explosion of a titanium foil with a weight powder sample of boron carbides with subsequent irradiation by a pulsed electron beam. The formation of an electroexplosive alloying zone of thickness up to 50 µm with a gradient structure, characterized by the decrease in the concentration of carbon and boron with increasing distance to the treatable surface has been revealed. Subsequent electron-beam treatment of the alloying zone leads to smoothing of the alloying area surface and is accompanied by the formation of a multilayer structure at a depth of 30 µm with alternating layers with different degrees of alloying having the structure at the submicro- and nanoscale level.


Articles with similar content:

STEEL 45 SURFACE MODIFICATION BY A COMBINED ELECTRON-ION-PLASMA METHOD
High Temperature Material Processes: An International Quarterly of High-Technology Plasma Processes, Vol.19, 2015, issue 1
I. A. Ikonnikova, Yu. A. Denisova, O. V. Ivanova, V. E. Gromov, Yurii F. Ivanov, E. A. Budovskikh, S. Yu. Filimonov
IRON ALLOYS SURFACE MODIFICATION BY PLASMA FORMED DURING ELECTRIC EXPLOSION OF ALUMINUM FOIL
High Temperature Material Processes: An International Quarterly of High-Technology Plasma Processes, Vol.17, 2013, issue 4
Yu. A. Denisova, V. E. Gromov, Yurii F. Ivanov, E. A. Budovskikh, S. Yu. Filimonov
MODIFICATION OF THE STRUCTURE AND PHASE COMPOSITION OF STRUCTURAL STEEL BY A MICROSECOND e-BEAM
High Temperature Material Processes: An International Quarterly of High-Technology Plasma Processes, Vol.17, 2013, issue 4
Vladimir N. Devyatkov, P. M. Schanin, Yu. A. Kolubaeva, Nikolay N. Koval, Yurii F. Ivanov, Olga V. Krysina
SYSTEMATIC STUDY OF STRUCTURAL AND CONDUCTIVE PROPERTIES OF COPPER NANOTUBES MODIFIED BY IONIZING RADIATION
Nanoscience and Technology: An International Journal, Vol.9, 2018, issue 2
I. Kenzhina, M. Kaikanov, M. Zdorovets, A. V. Tikhonov, Artem Kozlovskiy
STRUCTURE OF SURFACE LAYERS OF IRON AND CARBON STEELS TREATED BY COMPRESSION PLASMA FLOWS
High Temperature Material Processes: An International Quarterly of High-Technology Plasma Processes, Vol.8, 2004, issue 2
V. M. Anishchik, V. V. Astashynski, Vladimir V. Uglov, Iryna N. Rumiantseva