The Impact Factor measures the average number of citations received in a particular year by papers published in the journal during the two preceding years. 2017 Journal Citation Reports (Clarivate Analytics, 2018) IF: 0.4 The Immediacy Index is the average number of times an article is cited in the year it is published. The journal Immediacy Index indicates how quickly articles in a journal are cited. Immediacy Index: 0.1 The Eigenfactor score, developed by Jevin West and Carl Bergstrom at the University of Washington, is a rating of the total importance of a scientific journal. Journals are rated according to the number of incoming citations, with citations from highly ranked journals weighted to make a larger contribution to the eigenfactor than those from poorly ranked journals. Eigenfactor: 0.00005 The Journal Citation Indicator (JCI) is a single measurement of the field-normalized citation impact of journals in the Web of Science Core Collection across disciplines. The key words here are that the metric is normalized and cross-disciplinary. JCI: 0.07 SJR: 0.198 SNIP: 0.48 CiteScore™:: 1.1 H-Index: 20

Indexed in

INFLUENCE OF DC PLASMA PREHEATING ON OXIDE LAYERS FORMED BY FURNACE HEATING ON LOW CARBON STEEL SUBSTRATES AND RESULTING ADHESION/COHESION OF ALUMINA COATINGS

卷 7, 册 2, 2003, 11 pages
DOI: 10.1615/HighTempMatProc.v7.i2.100
Get accessGet access

摘要

In plasma spraying the preheating of low carbon steel substrates (X40) with a rough surface resulting from grit blasting, has received an increased interest because it promotes the adhesion and cohesion (A/C) of alumina coatings. Earlier works have reported the generation of a duplex Fе3O4/Fе2O3 layer after preheating by the d.c. plasma jet. Improved A/C values were obtained for an increase in Fе3O4 content in the oxide layer. Much improved adherence values were achieved with alumina spayed on Fe1-xO layers. In this case, the Adhesion/cohesion values obtained on smooth substrate (Ra ~ 0.1 mm) were good (~ 40 MPa) and close to those obtained on rough ones (Ra ~ 5 mm). First the time evolution of the Fe1-xO layer thickness and morphology produced in a controlled atmosphere furnace was studied. Then the influence of the plasma preheating of the wilstite layers was studied by SEM, and XRD analyses. XRD analysis results indicated a slight variation in the oxide phases depending on the preheating cycles. Fе3O4 was found to increase when a decomposition of Fe1-xO into Fе3O4 was observed.

对本文的引用
  1. Menecier S., Valette S., Denoirjean P., Lefort P., Invar® oxidation in CO2, Journal of Thermal Analysis and Calorimetry, 107, 2, 2012. Crossref

  2. Fauchais P., Montavon G., Plasma Spraying: From Plasma Generation to Coating Structure, in Advances in Heat Transfer Volume 40, 40, 2007. Crossref

  3. González Morales Noelia, Sánchez-Pérez Juan Francisco, Moreno Nicolás Jose Andres, Killinger Andreas, Modelling of Alumina Splat Solidification on Preheated Steel Substrate Using the Network Simulation Method, Mathematics, 8, 9, 2020. Crossref

Begell Digital Portal Begell 数字图书馆 电子图书 期刊 参考文献及会议录 研究收集 订购及政策 Begell House 联系我们 Language English 中文 Русский Português German French Spain